. 2023 Feb 26;15(3):771. doi: 10.3390/pharmaceutics15030771

Table 2.

Diameter by DLS and TEM, PDI, ζ-potential, and capacity of DOX-loaded nanocomposites Fe₃O₄@CaCO₃/DOX.

Fe₃O₄@CaCO₃ Amount, mg/mL	Hydrodynamic Diameter by DLS, nm	Diameter by TEM, nm			PDI	ζ-Potential, mV	Capacity, µg/mg	DOX Loading Efficiency, %	TEM Image Figure 6
Fe₃O₄@CaCO₃ Amount, mg/mL	Hydrodynamic Diameter by DLS, nm	NP	Agglomerate	Shell	PDI	ζ-Potential, mV	Capacity, µg/mg	DOX Loading Efficiency, %	TEM Image Figure 6
3.2	133 ± 3	—			0.234 ± 0.005	−14.7 ± 0.7	25± 1	79.7 ± 0.2	—
1.6	130 ± 2	—			0.192 ± 0.008	−13.0 ± 0.2	45 ± 2	74.7 ± 0.1	—
1.0	128 ± 3	10 ± 2	75 ± 13	4.6 ± 0.3	0.144 ± 0.006	−18.8 ± 0.6	73.2 ± 0.4	73.2 ± 0.4	A
0.40	129 ± 3	—			0.130 ± 0.002	−14.9 ± 0.4	160 + 2	64.9 ± 0.6	—
0.20	135 ± 5	11 ± 3	125 ± 31	18 ± 2	0.14 ± 0.01	−15.0 ± 0.3	295 + 2	59.4 ± 0.3	B
0.10	111 ± 3	9 ± 3	149 ± 45	46 ± 9	0.30 ± 0.01	−16.5 ± 0.3	525 ± 3	52.4 ± 0.4	C
0.050	113 ± 5	9 ± 5	201 ± 35	158 ± 46	0.28 ± 0.03	−12.4 ± 0.2	1045 ± 10	45 ± 2	D
0.025	105 ± 3	—			0.29 ± 0.01	−19.0 ± 0.5	1900 ± 27	34 ± 4	—
Initial Fe₃O₄@CaCO₃	121 ± 6	—			0.31 ± 0.01	−15.6 ± 0.5	—	—	—