Table 2.

Characterisation values of different films.

	KGL	CMK-Ⅰ	CMK-Ⅱ	CMKH-Ⅰ	CMKH-Ⅱ	CMKP-Ⅰ	CMKP-Ⅱ
Total phenolic content (mg CAE/g film)	–	–	–	37.00 ± 0.13^a	38.68±±0.78^a	–	–
Thickness (mm)	0.062 ± 0.001^d	0.086 ± 0.007^c	0.097 ± 0.006^b	0.102 ± 0.005^ab	0.109 ± 0.005^a	0.105 ± 0.002^ab	0.112 ± 0.002^a
Tensile strength (MPa)	10.01 ± 1.39^bc	8.11 ± 0.60^c	13.02 ± 2.23^ab	8.805 ± 0.44^c	8.03 ± 1.61^c	10.75 ± 0.56^abc	13.13 ± 1.47^a
Elongation at break (%)	61.33 ± 6.02^d	81.33 ± 2.63^b	55.43 ± 2.42^d	113.15 ± 1.83^a	83.13 ± 4.16^b	77.05 ± 3.14^bc	71.73 ± 0.52^c
Weight loss (%)	92.38 ± 1.09^c	85.28 ± 0.17^e	82.24 ± 0.49^f	88.24 ± 0.81^d	88.27 ± 0.66^d	95.15 ± 0.34^b	96.91 ± 0.11^a
Water vapor permeability (×10⁻¹⁰ g m⁻¹ s⁻¹ Pa⁻¹)	3.50 ± 0.16^a	3.02 ± 0.02^b	2.89 ± 0.10^b,c	2.89 ± 0.04^b,c	2.64 ± 0.12^c	3.34 ± 0.07^a	3.34 ± 0.23^a
Opacity (Abs/mm)	13.64 ± 1.34^b	12.03 ± 0.44^bc	10.84 ± 0.82^c	12.75 ± 0.73^b	11.06 ± 0.14^c	17.10 ± 0.80^a	16.86 ± 0.138^a
L*	90.72 ± 0.49^a	89.75 ± 0.37^b	88.84 ± 0.69^b,c	74.63 ± 0.56^d	74.36 ± 0.73^d	88.17 ± 0.62^c	87.83 ± 0.62^c
a*	−1.47 ± 0.04^d	−1.04 ± 0.09^c	−0.98 ± 0.05^c	2.45 ± 0.30^b	2.76 ± 0.46^a	−1.09 ± 0.21^c	−0.98 ± 0.13^c
b*	−0.17 ± 0.23^e	2.76 ± 0.94^d	3.88 ± 0.48^d	34.25 ± 0.46^b	36.29 ± 0.92^a	8.71 ± 1.34^c	9.95 ± 1.14^c
ΔE	1.54 ± 0.09^e	2.99 ± 0.84^d,e	4.01 ± 0.46^d	34.34 ± 0.48^b	36.41 ± 0.95^a	8.79 ± 1.31^c	10.00 ± 1.13^c

CAE, chlorogenic acid equivalent. The value is mean ± standard deviation (n = 3). Different letters in the same row indicate significant difference (p < 0.05).