Table 8.

Percent differences in mechanical properties (with original units provided) between the annealed and as-printed tensile specimens for each filament for both the optimal and worst-case parameter sets.

		Parameter Set	$\mathit{E}$ (MPa)	${\mathit{\sigma }}_{\mathit{y}}\left(\mathbf{MPa}\right)$	${\mathit{\sigma }}_{\mathit{U}\mathit{T}\mathit{S}}\left(\mathbf{MPa}\right)$	${\mathit{\epsilon }}_{\mathit{f}}(\%)$	$\frac{{\mathit{\sigma }}_{\mathit{U}\mathit{T}\mathit{S}}}{\mathit{m}}(\mathbf{MPa}/\mathbf{g})$
OVERTURE	White	Optimal	−3.51%	−6.34%	−6.5%	−13.39%	−6.61%
		Worst-Case	10.52%	12.71%	4.53%	−8.8%	−2.59%
	Black	Optimal	−8.4%	−7.41%	−9.79%	−9.19%	−9.9%
		Worst-Case	−18.69%	−1.22%	−2.67%	31.81%	−3.93%
	Green	Optimal	−7.51%	0.24%	−2.21%	18.34%	−4.82%
		Worst-Case	−13.21%	2.46%	1.56%	35.24%	−2.39%
SUNLU	White	Optimal	1.51%	−10.46%	−11.93%	−15.11%	−8.64%
		Worst-Case	0.55%	−2.09%	2.31%	−0.44%	0.02%
	Black	Optimal	−3.85%	5.11%	5.8%	7.97%	3.58%
		Worst-Case	5.33%	8.72%	9.64%	−4.56%	1.58%
	Green	Optimal	−9.97%	−17.78%	−16.78%	−11.22%	−13.2%
		Worst-Case	−11.45%	−10.14%	−11.08%	−1.12%	−5.69%
HATCHBOX	White	Optimal	4.15%	−7.69%	−7.64%	8.38%	−5.74%
		Worst-Case	−0.08%	−4.18%	−5.93%	2.86%	−5.35%
	Black	Optimal	3.58%	−4.96%	−7.15%	−10.15%	−6.24%
		Worst-Case	−7.44%	−1.03%	−1.56%	66.91%	−2.53%
	Green	Optimal	−6.6%	1.78%	−1.85%	−5.47%	−0.48%
		Worst-Case	6.97%	11.61%	6.49%	3.98%	2.15%