Table 2. Summary of the HER Performance of Rhenium-Based Selenides.
| system | mass loading (mg cm–2) | mass activity (A g–1) | overpotential (η10 in mV at 10 mA cm-2a) | Tafel slope (mV dec–1) | ref |
|---|---|---|---|---|---|
| ReSe2–x nanosheets | 102 | 67 | (137) | ||
| Re1–xMoS2 nanosheets | 77 | 42 | (154) | ||
| 1T′-ReSe2 nanoflakes | 0.5 | 20.00 | 60 | 37 | (155) |
| ReSe2(1–x)S2x/CFP | 0.44 | 22.72 | 84 | 123 | (156) |
| ReSe2/GF | 0.1 | 100 | 106 | 68 | (157) |
| ReSe2 nanoflakes/PCC | 140 | 64 | (158) | ||
| ReSe2 nanosheets/carbon cloth | 265 | 69 | (159) | ||
| ReSe2 microspheres | 67.5 | 80 | (160) | ||
| ReSe2 nanoflakes/rGO | 0.21 | 47.61 | 145.3 | 40.7 | (161) |
| ReS2xSe2(1–x) nanodots | 84 | 50.1 | (162) |
a
Current density at which the overpotential was measured is explicitly mentioned when it differs from 10 mA cm–2.