Figure 30.

Figure 30

MOR studied at NPG obtained from Ag77Au22Pt1 at 298 K, current densities are calculated with respect to the true surface area. (a) Variation of scan rate; 1 mol L–1 MeOH + 5 mol L–1 KOH in quiescent solution. (b) Variation of solution agitation by an external stirrer, v = 10 mV s–1, 1 mol L–1 MeOH + 5 mol L–1 KOH. (c) Variation of the positive vertex potential, v = 10 mV s–1, 1 mol L–1 MeOH + 5 mol L–1 KOH, quiescent solution. (d) Influence of MeOH concentration, v = 10 mV s–1, MeOH + 5 mol L–1 KOH, quiescent solution. Reproduced with permission from ref (525). Copyright 2016 Springer.