Table 3. Tensile test results of P-type and S-type specimens.

Specimens	Yield strength (MPa)	Tensile strength (MPa)	Elongation (%)	Max von Mises stress (MPa)
P-type 20% 2 mm	-	759	0.9	46.2
P-type 40% 2 mm	525	567	3.8	99.5
P-type 60% 2 mm	364	394	2.4	342.3
P-type 80% 2 mm	211	235	2.4	961.6
S-type 10% 2 mm	863	913	5.7	37.9
S-type 20% 2 mm	734	766	1.7	46.2
S-type 30% 2 mm	674	701	1.7	60.5
S-type 40% 2 mm	566	600	2.8	55.9
S-type 50% 2 mm	483	513	3.9	57.5
2mm L0P45	85	117	2.4	-
2mm L45P0	81	107	2.6	-
3mm L0P0	2.5	3.0	2.6	-
3mm L0P45	27	42	3.1	-