Table 2.

The mass gain and oxidation kinetics data of samples with different sintering holding time.

Holding Time(h) dTiC(μm) Mass Gain (mg•cm−2) kp (mg2•cm−4•h−1)
2 1.54 7.47 5.49 × 10−1
4 2.01 7.63 5.83 × 10−1
6 2.40 8.45 7.02 × 10−1