. 2021 Oct 6;1:120. [Version 1] doi: 10.12688/openreseurope.13716.1

Table 1. Mechanical properties and rheological behaviour: hardness shore A (HA); tensile strength (TS) [MPa]; elongation (EL) [% ]; specific gravity (SG) [g/cm ³]; initial peak (Init) [dNm]; moment lowest (ML) [dNm]; moment highest (MH) [dNm]; time to reach 90% MH (t90) [min.].

Rubber	HA	TS	EL	SG	Init	ML	MH	t90
NBR70	67	20.0	524	1.22	19.83	11.13	38.39	5.15
NBR80	75	14.5	260	1.28	22.57	10.82	39.32	5.37
NBR90	80	17.8	301	1.26	18.62	7.63	38.18	3.59
EPDM70	68	15.0	258	1.13	14.29	5.48	43.90	7.28
EPDM80	77	15.8	261	1.12	20.49	11.34	52.33	7.38
EPDM90	90	23.0	206	1.20	22.09	9.26	55.97	5.59
FKM70	76	12.0	230	1.90	14.98	4.68	32.77	3.72
FKM80	80	7.4	203	1.88	14.77	4.27	28.16	3.58
FKM90	88	14.0	117	1.91	25.59	8.25	70.43	3.91

Table 1. Mechanical properties and rheological behaviour: hardness shore A (HA); tensile strength (TS) [MPa]; elongation (EL) [% ]; specific gravity (SG) [g/cm 3]; initial peak (Init) [dNm]; moment lowest (ML) [dNm]; moment highest (MH) [dNm]; time to reach 90% MH (t90) [min.].