Table 6.
Post hoc tests for flexural strength
| Flexural strength | Group (I) | Group (J) | Mean difference (I–J) | Standard error | p-value |
|---|---|---|---|---|---|
| Maximum force (N) | Zirconomer | Composite | −11.47108* | 1.55073 | 0.000 |
| Cention N | −11.03189* | 1.55073 | 0.000 | ||
| Composite | Zirconomer | 11.47108* | 1.55073 | 0.000 | |
| Cention N | 0.43919 | 1.55073 | 0.957 | ||
| Cention N | Zirconomer | 11.03189* | 1.55073 | 0.000 | |
| Composite | −0.43919 | 1.55073 | 0.957 | ||
| Flexure displacement at maximum force (mm) | Zirconomer | Composite | −0.13649* | 0.04554 | 0.009 |
| Cention N | −0.36216* | 0.04554 | 0.000 | ||
| Composite | Zirconomer | 0.13649* | 0.04554 | 0.009 | |
| Cention N | −0.22568* | 0.04554 | 0.000 | ||
| Cention N | Zirconomer | 0.36216* | 0.04554 | 0.000 | |
| Composite | 0.22568* | 0.04554 | 0.000 |