Table 2.
Non-irradiation oxidation experiment data in SCW at operating temperature (T < 1000 °C).
| Composition (wt.%) |
Experimental Condition | Corrosion Products |
Thickness (μm) | Ref. | ||
|---|---|---|---|---|---|---|
| Temperature (°C) |
Time (h) |
Environment | ||||
| 430 SS (Commercial Fe–Cr alloy) |
500 | 1000 | SCW | Outermost: Fe2O3 Outer: Fe3O4 Inner: (Fe,Cr)3O4 |
≥15 | [64] |
| 16Cr–4Al | 550 | 250 | SCW | Outer: hematite, magnetite Inner: Al2O3 |
0.1 | [63] |
| 16Cr–3Al (Fe–15.98Cr–2.64Al–0.42Zr–0.29Y2O3) |
600 | 200 | SCW | Outer: Hexagonal (Cr, Fe)2O3 Inner: Al2O3 |
0.25 | [65] |
| 400 | -- | |||||
| 600 | 0.35 | |||||
| 800 | -- | |||||
| 1000 | 0.4 | |||||
| SOC–1 (Fe–16.11Cr–3.44Al–0.09Ti–0.34Y2O3) |
400 | 8760 (1Y) |
SCW | Outermost: Fe2O3 Outer: Al2O3, Inner: (Fe,Cr)3O4 |
-- | [64] |
| 500 | -- | |||||
| 600 | 5 | |||||