Table 3.

Process condition prediction results for STS 316 L powder and their respective relative density of the manufactured specimens measured through experiments

#	Laser power [W]	Scan speed [mm/s]	Layer thickness [mm]	Hatch spacing [mm]	Relative density [%]
1	341	1000	0.05	0.103	99.9
2	273	830	0.05	0.1	99.9
3	234	900	0.05	0.08	99.9
4	335	860	0.05	0.148	99.9
5	358	730	0.05	0.124	99.9
6	340	1540	0.05	0.084	99.8
7	395	740	0.05	0.155	99.8
8	398	1010	0.05	0.118	99.8
9	390	650	0.05	0.188	99.5
10	275	690	0.05	0.152	99.5
11	141	620	0.05	0.082	99.4
12	381	1320	0.05	0.093	98.9