Table 4.

Process condition prediction results for AlSi10Mg powder and their respective average relative density of the manufactured specimens measured through experiments

#	Laser power [W]	Scan speed [mm/s]	Layer thickness [mm]	Hatch spacing [mm]	Relative density [%]
1	398	2150	0.05	0.081	99.93
2	343	1600	0.05	0.105	99.9
3	314	1370	0.05	0.119	99.88
4	391	1540	0.05	0.083	99.87
5	322	1320	0.05	0.08	99.78
6	397	1470	0.05	0.118	99.71
7	272	1260	0.05	0.143	99.7
8	368	1250	0.05	0.097	99.57
9	236	990	0.05	0.131	99.48
10	278	1230	0.05	0.098	99.43
11	321	980	0.05	0.104	99.3
12	362	1270	0.05	0.148	98.12