Table 5.

Process condition prediction results for Fe60Co15Ni15Cr10 MEA powder and their respective average relative density of the manufactured specimens measured through experiments

#	Laser power [W]	Scan speed [mm/s]	Layer thickness [mm]	Hatch spacing [mm]	Relative density [%]
1	302	980	0.05	0.103	99.97
2	365	1010	0.05	0.118	99.90
3	282	780	0.05	0.122	99.90
4	349	1070	0.05	0.087	99.90
5	367	740	0.05	0.156	99.86
6	399	840	0.05	0.102	99.86
7	244	790	0.05	0.098	99.84
8	397	920	0.05	0.14	99.83
9	289	540	0.05	0.151	99.78
10	373	530	0.05	0.183	99.69
11	392	550	0.05	0.219	99.65
12	385	1380	0.05	0.094	99.06