Table 2.
Polymer | µ e,OTFT a) [cm2 V−1 s−1] | σ b) [S cm−1] | S c) [µV K−1] | PF c) [µW m−1 K−2] |
---|---|---|---|---|
PO8 | 0.015 (0.013 ± 0.02) | 18.1 (17.5 ± 0.4) | −110.2 (−107.2 ± 2) | 14.7 (13.1 ± 1.2) |
PO12 | 0.013 (0.010 ± 0.03) | 92.0 (90.1 ± 3) | −162.6 (−158 ± 2) | 94.3 (92.5 ± 2) |
PO16 | 0.007 (0.005 ± 0.001) | 43.5 (40.1 ± 0.5) | −95.4 (−92.1 ± 1) | 62.1 (57.8 ± 4) |
Electron mobility from OTFT devices
The conductivity of the polymers n‐doped at the optimal N‐DMBI concentration
The power factors and the corresponding Seebeck coefficient values. The average values in parenthesis are from at least five devices.