. 2023 Nov 20;15(48):56587–56599. doi: 10.1021/acsami.3c14348

Table 1. Values of Time Constants (τi), Normalized to 100 Amplitudes (a_i), and Contributions (c_i) Obtained from the Analysis of the Emission Decays of UiO-66-(OH)₂ in Powder Form upon Excitation at 371 nm and Observation As Indicated (Estimated Error Is around 10–15%).

sample	λ_obs (nm)	τ₁/ps	a₁	c₁	τ₂/ps	a₂	c₂
UiO-66-(OH)₂ solid state	425	45	83	57	170	17	43
	435	45	86	62	170	14	38
	450	45	84	59	170	16	41
	475	45	81	53	170	19	47
	500	52	79	47	216	21	53
	550	70	69	36	272	31	64
	600	70	70	37	272	30	63
	650	70	67	34	272	33	66

Table 1. Values of Time Constants (τi), Normalized to 100 Amplitudes (ai), and Contributions (ci) Obtained from the Analysis of the Emission Decays of UiO-66-(OH)2 in Powder Form upon Excitation at 371 nm and Observation As Indicated (Estimated Error Is around 10–15%).