Table 2.
XRD analysis results for various MOFs.
| MOF | Crystal Size | XRD Technique | Structural Formula | Reference |
|---|---|---|---|---|
| MIL-96 (Al) | 0.04 × 0.04 × 0.04 (mm3) | Single-crystal X-ray | Al12O(OH)18(H2O)3(Al2(OH)4) [btc]6·24H2O | [56] |
| MOF-5 | 0.1 × 0.1 × 0.18 (mm3) | Single-crystal X-ray | Zn4O(BDC)3·(DMF)8(C6H5Cl) | [57] |
| UiO-66(Zr) | 2 × 2 × 2 (μm3) | PXRD | Zr24 O120 C192 H96 | [58] |
| MOF-892 | 0.14 × 0.09 × 0.08 (mm3) | Single-crystal X-ray | Zr6O4(OH)4(CH3CO2)6(CO2)6 | [59] |
| CPO-27-Co | 0.02 × 0.02 × 0.20 (mm3) | Single-crystal X-ray | [Co2(C8H2O6) (H2O)2]·8H2O | [60] |
| NOTT-112 | 0.05 × 0.05 × 0.05 (mm3) | Single-crystal X-ray | [Cu3(C54H24O12) (H2O)3] ·16DMF·26H2O | [61] |
| MOF-73 | 0.2 × 0.1 × 0.05 (mm3) | Single-crystal X-ray | Mn3(BDC)3 (DEF)2 | [62] |
| MOF–72 | 0.3 × 0.1 × 0.1 (mm3) | Single-crystal X-ray | Cd3 (1,3–BDC)4•(Me2NH2)2 | [62] |
| MOF-70 | 0.22 × 0.20 × 0.18 mm | Single-crystal X-ray | Pb (BDC) (C2H5OH)·(C2H5OH) | [62] |
| TUDMOF-1 | 60–70 nm | PXRD | Mo3(BTC)2 | [63] |
| MOF-48 | 0.10 × 0.10 × 0.05 (mm3) | Single-crystal X-ray | VO(DMBDC)·(H2DMBDC)0.4 | [64] |
| Ni-MOF-74 | (2.8 nm) | PXRD | Ni2(dhtp) (H2O)2·8H2O | [65,66] |
| MIL-53(Al) | (4 μm) | PXRD | Al(OH)[O2C–C6H4–CO2]⋅[HO2C–C6H4–CO2H]0.70 | [4,33] |
| MIL-101 | 8.87 × 8.87 × 8.87 (nm3) | PXRD | Cr3OH(H2O)2O(BDC)3 | [67] |
| UiO-67 | 75 μm | Single-crystal X-ray | Zr6C84H48O32 | [68,69] |
| POST-1 | 0.15 × 0.5 × 0.5 (mm3) | PXRD + Single-crystal X-ray | Zn3 (μ3-O) (D-PTT)6 | [70] |
| MIL-125 | 210–660 nm | PXRD | Ti16O72C96H64 | [71,72] |
| MIL-100(Fe) | <200 nm | PXRD | Fe3O(H2O)2F·(C6H3(CO2)3)2·nH2O | [8,73] |
| ZIF-8 | 0.16 × 0.10 × 0.10 mm3 | Single-crystal X-ray | C24 H30 N12 O10 Zn3 | [32] |
Materials Institute Lavoisier; UiO = University of Oslo; CPO = Coordination polymer of Oslo; NOTT = Nottingham University; TUDMOF-1 = Technical University of Dresden Metal-Organic Framework, POST = Pohang University of Science and Technology.