Figure 2.

Figure 2

Point defect type exploration for 200 °C-vacuum-annealed 2H-MoTe2 (VA 2H-MoTe2) ML. (a) Wide-view HAADF-STEM image of VA 2H-MoTe2 ML. Typical defects denoted by dotted rectangles (i)–(iv) in (a) represent VTe1, VTe2, Tead1, and Tead2, respectively. (b)–(e) (Top panels) Enlarged HAADF-STEM micrographs, revealing (i) VTe1 (dotted red circle), (ii) VTe2 (dotted yellow circle), (iii) Tead1 (solid light-green circle), and (iv) Tead2 (orange solid circle), respectively. (Bottom panels) Corresponding atomic models as top panels; VTe1 (VTe2) with red (yellow) dotted circle and Tead1 (Tead2) with solid light-green (orange) spheres, respectively. Scale bars: 0.2 nm.