Table 4.

The stress-strain properties used for grading purposes are summarized for specimens manufactured via an X-only laser scan strategy. The average and standard deviation values are provided (sample size is N=12), which take into consideration specimens from different manufactured blocks. Refer to Section 2.3 for information about the specimen notation used here. Some tests were invalid (INV) due to failure occurring outside of the gauge length.

	Unit	$\mathrm{X}-\mathbb{A}-0^{\circ }-\mathbb{A}$	$\mathrm{X}-\mathbb{A}-{30}^{\circ }-\mathbb{A}$	$\mathrm{X}-\mathbb{A}-{45}^{\circ }-\mathbb{A}$	$\mathrm{X}-\mathbb{A}-{60}^{\circ }-\mathbb{A}$	$\mathrm{X}-\mathbb{A}-{90}^{\circ }-\mathbb{A}$
E	GPa	164.7 ± 11.6	INV	INV	172.2 ± 11.5	127.4 ± 11.0
σY	MPa	620.7 ± 10.1	INV	INV	692.9 ± 8.9	701.5 ± 4.7
σ 0.05	MPa	729.5 ± 5.4	INV	INV	827.7 ± 7.8	851.8 ± 5.0
σ 0.10	MPa	792.6 ± 5.7	INV	INV	923.0 ± 8.4	967.4 ± 8.5
σ 0.20	MPa	925.1 ± 8.5	INV	INV	1095.9 ± 11.8	1151.8 ± 14.8
σUTS	MPa	1192.9 ± 37.8	INV	INV	1195.6 ± 24.6	1197.9 ± 23.9
εUTS	–	0.400 ± 0.016	INV	INV	0.271 ± 0.016	0.232 ± 0.008