Table 1.

Polymer film characterization^*

Samples	Tg (°C)	Tm₁ (°C)	Tm₂ (°C)	Peak stress (MPa)	Breaking strain (%)	Initial modulus (MPa)	Inherent viscosity (dL/g)	Water absorption (%)	Instant recovery (%)
PU-BDO	−58	26	-	12.3±0.8	729±126^a	15±2^a	1.72	43±5^a	99±1
PU-0.5SS	−60	36	-	12.2±1.4	1021±274^a	4±1^b	2.43	32±16^a	100±1
PU-1SS	−59	35	-	11.9±0.5	1098±231^a	8±1^c	2.32	40±7^a	99±1
PU-1.5SS	−59	16	110	12.0±0.6	821±116^a	26±4^b	1.72	67 ±4^b	99±1
PU-1.8SS	−57	-	126	11.5±1.4	337±45^b	44±3^e	1.63	76±10^b	98±1

^{*a, b, c, d, e}

represent significantly different groups for each characteristic.