. 2024 May 3;16(19):25529–25539. doi: 10.1021/acsami.4c01741

Table 1. Summary of Optical Properties, where E_g^abs and E_g^cal are the Band Gaps Acquired through Elliot Fitting, as Illustrated in Figure S2, and DFT Calculation, as Depicted in Figure 2, Respectively.

compounds	E_g^cal (eV)	E_g^abs (eV)	maximum PL peak (eV)	Stokes shift (E_g^abs ∼ Max.^PL), (eV)	fwhm (eV)
(PEA)₂PbBr₄	2.92	2.96	3.00	0.04	0.26
(PEA_1.5BZA_0.5)PbBr₄	2.97	3.02	3.01	0.01	0.23
(PEABZA)PbBr₄	3.00	3.04	3.01	0.03	0.25
(BZA)₂PbBr₄	3.05	3.09	3.03	0.06	0.21

Table 1. Summary of Optical Properties, where Egabs and Egcal are the Band Gaps Acquired through Elliot Fitting, as Illustrated in Figure S2, and DFT Calculation, as Depicted in Figure 2, Respectively.