Table 2. CHN Chemical Composition of Selected As-Made and O₃-Treated Samples.

zeolite		T (°C)a	timeb	C (%)	H (%)	N (%)
SiO2-2E134TMI-STW	as-made		0	12.66	1.99	3.69
		200	72 h	0.92	0.27	0.38
(Ge,Si)O2-10BDMI-HPM-8	as-made		0	11.82	1.80	2.76
		100	20 h	4.14	1.08	1.58
(Ge,Si)O2-10BDMI-POS	as-made		0	11.22	1.71	2.62
		100	20 h	6.46	1.56	1.96
(Ge,Si)O2-1M3TMBI-HPM-14	as-made		0	11.15	1.57	2.71
		100	20 h	2.10	1.58	2.46
(Ge,Si)O2-1M2E3PrI-HPM-16	as-made		0	10.26	1.95	2.63
		100	5 min	7.29	1.89	2.40
		100	20 h	1.57	1.36	2.18
		150	50 h	0.28	0.84	0.16
(Ge,Si)O2-1M2E3PrI--SYT	as-made		0	12.79	2.72	3.35
		100	6 h	9.50	2.40	3.04
		100	20 h	7.51	1.79	2.50
		100	30 h	2.15	1.30	2.94
SiO2-4BI-MFI	as-made		0	7.50	1.29	3.19
		150	24 h	0.82	0.52	0.60
SiO2-EABO-ISV	as-made		0	14.89	2.40	1.23
		180	84 h	3.62	0.66	0.32
SiO2-4bBnMI-beta	as-made		0	17.46	2.10	3.04
		100	20 h	5.68	0.97	2.07
SiO2-8bDMI-beta	as-made		0	11.80	1.97	2.78
		150	6 h	5.51	0.96	1.12

^aTemperature.

^bTime of the O₃ treatment for the treated samples. Temperatures higher than 100 °C were only applied when long treatments at 100 °C did not afford significant detemplation.