. 2024 Jun 21;9(26):28637–28647. doi: 10.1021/acsomega.4c02827

Table 1. Porosity Obtained via N₂ Sorption Experiments and Metal Composition Obtained via ICP-OES of the Calcined Catalysts^a.

catalyst	N₂ sorption		metal content^d			Pt/Ni^d mole ratio
	S_BET (m² g^–1)^a	V_p (cm³ g^–1)^b	D_p (nm)^c	Ni (wt %)	Pt (wt %)
Ni/Al₂O₃	187	0.50	7.4	9.69	0
Pt/Al₂O₃	207	0.51	7.4	0	10.58
Ni₁Pt_0.004/Al₂O₃	164	0.42	7.4	9.6	0.126	0.004
Ni₁Pt_0.007/Al₂O₃	148	0.40	7.4	10.16	0.242	0.007
Ni₁Pt_0.015/Al₂O₃	149	0.38	7.4	11.54	0.584	0.015

S_BET obtained from the adsorption branch of the N₂ isotherm.

V_p calculated from N₂ adsorption at a relative pressure of ∼0.990.

D_p obtained from the desorption branch via the BJH method.

Table 1. Porosity Obtained via N2 Sorption Experiments and Metal Composition Obtained via ICP-OES of the Calcined Catalystsa.