Table 8.
Mass proportions of printed test specimens made of coated and uncoated filaments in wt%.
| Sample |
A05 |
A06 |
A07 |
E05 |
E06 |
E07 |
B05 |
B06 |
B07 |
F05 |
F06 |
F07 |
C05 |
C06 |
C07 |
G05 |
G06 |
G07 |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Elements | PETG | PETG | PETG | PLA | PLA | PLA | PETG + nHA | PETG + nHA | PETG + nHA | PLA + nHA | PLA + nHA | PLA + nHA | PETG + nFA | PETG + nFA | PETG + nFA | PLA + nFA | PLA + nFA | PLA + nFA |
| C | 53.83 | 60.87 | 55.30 | 34.36 | 36.05 | 39.07 | 19.03 | 19.48 | 11.99 | 12.93 | 7.69 | 16.58 | 11.13 | 39.78 | 12.74 | 32.08 | 36.73 | 33.39 |
| N | 2.63 | 2.98 | 2.41 | 2.86 | 3.97 | 2.96 | 7.26 | 3.97 | 3.17 | 2.80 | 3.27 | 3.80 | 2.98 | 5.10 | 3.89 | 4.23 | 3.35 | 4.75 |
| O | 24.83 | 21.17 | 25.87 | 39.49 | 37.69 | 36.84 | 38.76 | 20.42 | 27.93 | 34.25 | 37.99 | 31.25 | 30.69 | 23.66 | 36.04 | 37.79 | 26.65 | 32.77 |
| F | 1.55 | 2.99 | 2.77 | 1.84 | 1.09 | 0.79 | 1.33 | 1.45 | ||||||||||
| Na | 1.60 | 0.39 | 0.59 | 0.68 | 0.64 | 0.74 | 0.17 | 0.52 | 0.59 | 0.57 | ||||||||
| P | 9.92 | 12.21 | 10.90 | 9.02 | 10.48 | 3.69 | 9.53 | 0.40 | 1.52 | 1.65 | ||||||||
| Al | 4.00 | |||||||||||||||||
| Au | 18.71 | 14.98 | 16.41 | 16.86 | 16.07 | 15.56 | 13.54 | 18.55 | 16.02 | 17.42 | 17.61 | 16.78 | 18.82 | 16.09 | 15.49 | 16.63 | 18.18 | 15.33 |
| Cl | 0.78 | |||||||||||||||||
| K | 2.19 | |||||||||||||||||
| Ca | 6.48 | 6.23 | 5.57 | 12.84 | 25.72 | 25.09 | 32.60 | 22.54 | 21.89 | 22.51 | 9.10 | 21.04 | 7.56 | 11.65 | 10.09 |
Note: Percentages represent mass fractions (Wt%). Values are rounded.
Abbreviations: Carbon (C), Nitrogen (N), Oxygen (O), Fluorine (F), Sodium (Na), Phosphorus (P), Aluminum (Al), Gold (Au), Chlorine (Cl), Potassium (K), Calcium (Ca).