. 2024 Aug 6;9(33):35937–35949. doi: 10.1021/acsomega.4c05212

Table 5. Glass Transition Temperature (T_g), Cold Crystallization Temperature (T_cc), Melt Temperature (T_m), and Crystallinity (X_c) of Neat PLA, PLA_BL20, and PLA_BL20-g-5GMA, Obtained from the DSC 2nd Heating Cycle after Cooling with Different Rates.

composite	cooling rate (°C/min)	T_g (°C)	T_cc (°C)	ΔH_cc (J/g)	T_m (°C)	ΔH_m (J/g)	X_c (%)
neat PLA	5	58.27	104.00	22.53	144.29	24.06	1.64
	2.5	59.07	104.65	21.14	144.43	24.07	3.13
	1	60.19	100.42	2.67	142.33	25.98	23.97
PLA_BL20	5	54.93	111.68	5.43	144.48	5.89	0.49
	2.5	56.04	112.00	3.89	144.71	4.26	0.39
	1	57.82	112.49	1.28	145.12	1.79	0.54
PLA_BL20-g-5GMA	5	54.18	108.54	13.16	142.59	13.88	0.77
	2.5	55.95	108.60	13.78	143.17	14.80	1.10
	1	57.43	112.81	5.04	144.58	6.15	1.19

Table 5. Glass Transition Temperature (Tg), Cold Crystallization Temperature (Tcc), Melt Temperature (Tm), and Crystallinity (Xc) of Neat PLA, PLA_BL20, and PLA_BL20-g-5GMA, Obtained from the DSC 2nd Heating Cycle after Cooling with Different Rates.