Table 6.
The results of adsorption thermodynamic of organic scaffolds on CS in 1.0 M HCl at 303- 323 K
| Inhibitors | Temp K |
Kads M−1 | − ΔG°ads kJ mole−1 | -ΔH°ads kJ mole−1 | -ΔS°ads J mole−1 k−1 |
|---|---|---|---|---|---|
| HM-1223 | 303 | 5.55E + 02 | 26.1 ± 0.1854 | 67.3 ± 0.2142 | 136.149 ± 0.1214 |
| 308 | 4.10E + 02 | 25.6 ± 0.1565 | 135.061 ± 0.1254 | ||
| 313 | 2.41E + 02 | 24.7 ± 0.1254 | 135.99 ± 0.1412 | ||
| 318 | 1.48E + 02 | 23.8 ± 0.2124 | 136.664 ± 0.1214 | ||
| 323 | 1.17E + 02 | 23.5 ± 0.2144 | 135.342 ± 0.1754 | ||
| HM-1222 | 303 | 4.44E + 02 | 25.5 ± 0.1524 | 54.9 ± 0.1624 | 97.126 ± 0.1214 |
| 308 | 3.04E + 02 | 24.9 ± 0.1247 | 97.3341 ± 0.1234 | ||
| 313 | 2.48E + 02 | 24.8 ± 0.1124 | 96.1793 ± 0.1425 | ||
| 318 | 1.45E + 02 | 23.7 ± 0.1124 | 97.884 ± 0.1652 | ||
| 323 | 1.19E + 02 | 23.6 ± 0.1414 | 96.8543 ± 0.1722 | ||
| HM-1224 | 303 | 1.33E + 02 | 22.4 ± 0.1474 | 30.1 ± 0.1244 | 25.4227 ± 0.1241 |
| 308 | 1.08E + 02 | 22.2 ± 0.1452 | 25.5391 ± 0.1785 | ||
| 313 | 8.79E + 01 | 22.1 ± 0.1147 | 25.688 ± 0.1652 | ||
| 318 | 7.54E + 01 | 22.0 ± 0.1457 | 25.4493 ± 0.1254 | ||
| 323 | 6.31E + 01 | 21.9 ± 0.1425 | 25.4628 ± 0.1325 | ||
| HM-1221 | 303 | 7.78E + 01 | 21.1 ± 0.1752 | 27.3 ± 0.1412 | 20.3729 ± 0.1574 |
| 308 | 5.99E + 01 | 20.8 ± 0.1365 | 21.0864 ± 0.1475 | ||
| 313 | 4.86E + 01 | 20.5 ± 0.1245 | 21.4108 ± 0.1547 | ||
| 318 | 4.17E + 01 | 20.4 ± 0.1514 | 21.3145 ± 0.1874 | ||
| 323 | 3.19E + 01 | ± 0.1321 | 22.2151 ± 0.1958 |