Table 3.

Ultimate Tensile Strength, Elongation at Break, and Young’s Modulus with standard deviations of PP Films with additives.

Films	Ultimate Tensile Strength, (MPa)	Elongation at Break, (%)	Young’s Modulus (GPa)
PP BLK	29.36 ± 0.47	4.20 ± 0.08	1.71 ± 0.07
0.5 wt% GN	18.20 ± 1.13	1.37 ± 0.19	1.83 ± 0.16
0.5 wt% BIOC	29.94 ± 0.83	3.70 ± 0.42	1.87 ± 0.04
2 wt% BIOC	31.45 ± 0.50	3.47 ± 0.29	2.20 ± 0.10
0.5 wt% HEM	16.24 ± 2.88	1.40 ± 0.00	1.78 ± 0.09
2 wt% HEM	11.91 ± 1.60	0.73 ± 0.21	2.12 ± 0.05
0.5 wt% ROCH	8.00 ± 3.30	0.40 ± 0.08	1.91 ± 0.21
2 wt% ROCH	6.00 ± 2.62	0.40 ± 0.16	1.85 ± 0.09