Table 1.
Comparison of electrochemical properties of Si/MXene composites synthesized by different methods
| Anodes | Method | Specific Capacity (mAh/g) | Cycling Stability (mAh/g) | Rate Capacity (mAh/g) | Reference | |
|---|---|---|---|---|---|---|
| Si/MXene | Physical Methods |
Mechanical ball mill | 3486.2 | 980.8 after 500 cycles at 0.5A/g | 632.4 at 5 A/g | Liu et al.77 |
| Ultrasound mixing | 1195 | 188 after 150 cycles at 0.2A/g | – | Kong et al.78 | ||
| Vacuum filtration | 2843.5 | 555.5 after 500 cycles at 1A/g | 840.3 at 5 A/g | Zhang et al.79 | ||
| Spray drying | 2610 | 550 after 200 cycles at 1.7A/g | – | Sarang et al.80 | ||
| Coaxial electrospinning | 1377.8 | 540 after 100 cycles at 0.1A/g | 301.1 at 2 A/g | Jiang et al.81 | ||
| Freeze drying | 2395.1 | 1203.3 after 100 cycles at 0.2A/g | 1046.1 at 2 A/g | Yang et al.82 | ||
| Chemical methods | Hydrothermal | 3257 | 1422 after 200 cycles at 0.5A/g | 574 at 5 A/g | Li et al.83 | |
| Electrostatic assembly | 3502.3 | 1342.8 after 200 cycles at 1A/g | 1515.8 at 3 A/g | Yang et al.84 | ||
| Anneal | 2554 | 953 after 300 cycles at 1A/g | 849 at 1 A/g | Jo et al.85 | ||
| Heat treatment and Self assembly | 3388.9 | 984.9 after 800 cycles at 1A/g | 1033.6 at 2 A/g | Liu et al.86 | ||
| Magnesium thermal reduction |
2517 | 939 after 100 cycles at 0.5A/g | – | Jiang et al.87 | ||
| 1674 | 390 after 1000 cycles at 42A/g | 398 at 42 A/g | Zhang et al.88 | |||