Experimental results of energy bandgaps, % of crystallinity, average crystallite size and average micro strain of fabricated Ti4AlB2N and Ti4AlB2C sample composites.

Sample name Sintering temperature (°C) Energy bandgap (eV) % of crystallinity Average crystallite size, D (nm) Average dislocation density Average microstrain, (ε) δ
Ti4AlB2N 950 2.33 69.14479301 33.4801158 0.000892126 0.174
1050 2.11 68.49341763 28.75657405 0.001209277 0.3706
1150 2.00 80.98498124 28.22378443 0.001255364 0.1905
1250 1.73 89.87724096 33.25336288 0.000904334 0.1809
1325 2.12 84.49385884 51.74103091 0.000373534 0.13325
Ti4AlB2C 950 2.60 71.02942065 32.14693379 0.000967656 0.1954
1050 2.48 58.43002545 38.47868919 0.000675398 0.214
1150 2.43 77.85832197 23.68582858 0.001782472 0.2405
1250 2.40 72.7525578 25.37922385 0.001552542 0.2148
1325 2.55 75.72842043 49.78197252 0.000403511 0.1309