Table 2.
Mean values with standard deviations of fracture toughness (FT), flexural strength (FS), flexural modulus (FM), degree of conversion (DC), wear depth (WD), and shrinkage stress (SS)
| Material | FT (MPa m1/2) |
FS (MPa) |
FM (GPa) |
DC (%) |
WD (µm) |
SS (MPa) |
|---|---|---|---|---|---|---|
| Essentia U | 1.1 ± 0.1a | 121 ± 9ab | 12.9 ± 1.4c | 42.1 ± 1.9a | 24.5 ± 5ab | 2.5 ± 0.3a |
| Alert | 1.7 ± 0.4b | 118 ± 18ab | 9.9 ± 0.9bc | 61.8 ± 0.3c | 28.5 ± 2.4b | 3.7 ± 0.2b |
| Fibrafill Flow | 1.1 ± 0.07a | 92 ± 12a | 6.8 ± 0.3a | 54.7 ± 0.3b | 29.6 ± 1.6b | 3.5 ± 0.04b |
| Fibrafill Dentin | 1.2 ± 0.1a | 98 ± 9a | 9.5 ± 0.6b | 53.2 ± 0.6b | 35.3 ± 2.5bc | 3.2 ± 0.01b |
| everX Flow | 2.8 ± 0.4cd | 147 ± 23c | 9.0 ± 0.7b | 62.8 ± 0.3c | 20.4 ± 4.9a | 5.3 ± 0.6c |
| everX Posterior | 2.6 ± 0.4c | 120 ± 5ab | 12.6 ± 2.8c | 54.5 ± 1.5b | 30.7 ± 0.6b | 3.9 ± 0.2b |
Materials with the same superscript letter above the values were statistically similar (p > 0.05)