Table 2. The effect of concentration and temperature on the anticorrosion behavior of PBT for Q235 CS in 1.0 mol per L HCl.

T/K	C inh/mmol L−1	v/mg cm−2 h−1	η/%
288.15 K	Blank	0.5834 ± 0.0068
	0.005	0.3407 ± 0.0042	41.6%
	0.01	0.2187 ± 0.0048	62.5%
	0.05	0.1703 ± 0.0024	70.8%
	0.25	0.1340 ± 0.0034	77.0%
	1.0	0.0991 ± 0.0044	83.0%
298.15 K	Blank	2.2074 ± 0.0164
	0.005	1.1227 ± 0.0052	49.1%
	0.01	0.5832 ± 0.0086	73.6%
	0.05	0.2833 ± 0.0058	87.2%
	0.25	0.2370 ± 0.0110	89.3%
	1.0	0.2106 ± 0.0050	90.5%
308.15 K	Blank	3.5767 ± 0.0055
	0.005	1.9278 ± 0.0109	46.1%
	0.01	1.2272 ± 0.0133	65.7%
	0.05	0.8325 ± 0.0091	76.7%
	0.25	0.4121 ± 0.0079	88.5%
	1.0	0.3531 ± 0.0061	90.1%
318.15 K	Blank	7.0016 ± 0.0028
	0.005	4.5279 ± 0.0120	35.3%
	0.01	3.8737 ± 0.0093	44.7%
	0.05	2.4511 ± 0.0043	65.0%
	0.25	1.2649 ± 0.0102	81.9%
	1.0	0.7146 ± 0.0032	89.8%