2. Modulus, Strength at Break, and Elongation at Break of PA6 7 M LiI Filaments with 25× Draw Ratio at Different Stages Postprocessing.

sample	modulus (MPa)	strength at break (MPa)	elongation at break (%)
gel state (as extruded)	0.66 ± 0.0	-	2451.0 ± 131.0
sprayed, washed, and dried	2,035 ± 0.2	70.3 ± 5.7	19.7 ± 8.7
sprayed, washed, dried, postdrawn	18,700 ± 2.3	1143.2 ± 226.7	7.9 ± 1.7