Table 4.
Mechanical properties of related electrode materials
| Electrode material | Application | Young's modulus | Tensile strength (MPa) | Final strain (elongation) | Max bending (angle/radius) | Capacitance | Energy density | Bending cycle performance | References |
|---|---|---|---|---|---|---|---|---|---|
| CC/MoS2@C | SC | 175° | 108.3 mF cm−2 | 113% (5000 bends) | [63] | ||||
| V2O5-rGO | SC | 1.7 GPa | 6.1 | 3% | 145° | 511.7 mF cm−2 | 89 μW h cm−2 | [64] | |
| PANI-PPG | SC | 134.9 ± 34.3 kPa | 608.2% | Any angle | 95.8 mF cm−2 | 8.5 μWh cm−2 | > 90% (1000 bends) | [65] | |
| MXene-cellulose paper-MXene | SC | 0.6 cm | 77.25 mF cm−2 | [65] | |||||
| EG-PCPPH//CCPH-PPy | SC | 22.3 | 286% | 180° | 397.99 μWh cm−3 | 98% (1000 bends) | [66] | ||
| MXene/Au NPs | SC | 180° | 332 F g−1 | 1.35 μWh cm−2 | [67] | ||||
| LCO/PVDF/CNT | Battery | 1.3 GPa | 3 mm | [68] | |||||
| LCO/graphite | Li-ion battery | 70 MPa | 180° | 154.5 mAh g−1 | 242.21 Wh L−1 | 97.28% (5000 bends) | [69] | ||
| PDHBQ S-SWCNTs | Li-ion battery | 2.8 GPa | 20.1 | 2.5% | 2.1 cm | 182 mAh g−1 | 88% (2000 bends) | [70] | |
| PMTA/SWCNT | Li-ion battery | 10.6 MPa | 0.44 | 9.33% | 0.67 cm | 163 mAh g−1 | 80% (1000 bends) | [71] | |
| GCF/Cu/Li | Lithium Metal Full Battery | 2.5% | < 2 mm | 300 Wh kg−1 | > 95% (500 bends) | [72] | |||
| MnO2 NWs/SWNT/FLGs | Zn-ion battery | 25 | ~ 4.9% | 180°/1 mm | 374 mAh g−1 | 651.5 Wh kg−1 | 91.71% (75 bends) | [73] |