. 2005 Feb 20;6(3):213–218. doi: 10.1631/jzus.2005.B0213

Table 1.

Properties and crystalline phases of the composites

Samples Bulk density (g/cm3) Relative density (%) Fracture toughness (MPa·m1/2) Bending strength (MPa) Crystalline phases
Major Secondary
Sintered at 1860 °C 3.19 96.1 5.7 486 6H-SiC YAG
Sintered at 1950 °C 3.11 93.7 4.9 437 6H-SiC YAG
Sintered at 2000 °C 3.01 89.2 3.3 356 6H-SiC YAG