Published in final edited form as: Chem Mater. 2005 Aug 9;17(16):4256–4261. doi: 10.1021/cm0506858

Table 3.

Size Analysis of Sulfide-Treated Nanorodsa

t
(min)		 count
(N)		 length
L (nm)		 midsection
D1 (nm)		 end width
D2 (nm)		 width ratio
(D1/D2)		 aspect ratio
(L/D1)		 aspect ratio
(L/D2)
15  95 44.3 ± 13  11.5 ± 1.5 14.5 ± 1.9 0.79 ± 0.06 3.99 ± 0.83 3.17 ± 0.62
20 103 48.9 ± 7.7 13.2 ± 1.5 16.9 ± 1.6 0.80 ± 0.05 3.71 ± 0.71 2.98 ± 0.47
30 117  50.5 ± 7.5 13.7 ± 1.6 17.2 ± 1.9 0.80 ± 0.04 3.71 ± 0.63 2.96 ± 0.51
40  91   55.2 ± 11.0 18.6 ± 2.5 21.1 ± 3.2 0.89 ± 0.05 2.96 ± 0.65 2.63 ± 0.59
50 103 58.1 ± 6.3 21.4 ± 2.1 24.2 ± 2.5 0.89 ± 0.05 2.77 ± 0.41 2.45 ± 0.37
a

Nanorods were isolated by one C/R cycle in deionized water, prior to TEM sample preparation. Errors represent one standard deviation.