Glass transition temperatures, melting temperatures and Young’s modulus reported for PCL-based segmented PEUUR elastomers

Polymer	T_g (°C)	T_m (°C)	Modulus (MPa)
BDI/BDA/PCL1250 [36]	−37	A	54
BDI/BDA/PCL2000 [36]	−53	40	78
BDI/Lys/PCL1250 [36]	−40	A	14
BDI/Lys/PCL2000 [36]	−54	45	38
LDI/Phe/PCL530 [38]	−6	A	6.6
LDI/Phe/PCL1250 [38]	−34	43	54
LDI/Phe/PCL2000 [38]	−52	45	82
BDI/BDA/PCL2000 [34]	−57	20	52
HDI/BDA/PCL2000 [34]	−51	22	38
LDI/BDA/PCL2000 [34]	−52	41	40
BDI/BDO.BDI.BDO/PCL2000 [16]	−54	18	70

An ‘a’ denotes amorphous polymers that did not exhibit a PCL melting temperature.