Table 3.
Material | Density, ρ % th. | Flexural strength, σf (MPa) | Initiation toughness, KIC (MPa. √m) | Vickers hardness, Hv (GPa) | |
---|---|---|---|---|---|
3-point bending | Indentation | ||||
β-TCP | 99 | 102±13 | 1.16±0.16 | 1.28±0.32 | 4.737 |
HA | 97 | 77±20 | 0.72±20 | 0.91±0.23 | 4.880 |
BCP | 98 | 34±3.7 | - | 0.48±0.12 | 4.256 |