Table II.

Summary of the Mechanical Properties of the DCL-14 and the MCC Layers of the Sample Set

					Acoustic properties		Mechanical properties
Tablet No.	Layer	V (m3)	m (mg)	ρ (kg/m3)	c L (m/s)	c T (m/s)	E (GPa)	v	G (MPa)
Tablet01	DCL-14	120.43	149.12	1,238.22	2,142.85	1,315.31	5.69	0.33	2,142.17
	MCC	87.73	99.88	1,138.48	1,375.03	846.39	2.15	0.32	815.58
Tablet02	DCL-14	121.77	148.98	1,223.45	2,147.77	1,309.86	5.64	0.34	2,099.11
	MCC	87.94	100.19	1,139.33	1,373.28	845.32	2.15	0.32	814.13
Tablet03	DCL-14	120.14	149.28	1,242.55	2,143.46	1,316.47	5.71	0.33	2,153.46
	MCC	87.14	99.21	1,138.56	1,371.68	846.95	2.14	0.31	816.72
Tablet04	DCL-14	121.26	149.05	1,229.17	2,148.38	1,312.33	5.67	0.34	2,116.89
	MCC	88.02	100.23	1,138.71	1,370.31	845.12	2.14	0.32	813.30
Tablet05	DCL-14	120.29	149.19	1,240.25	2,143.41	1,316.91	5.70	0.33	2,150.91
	MCC	87.55	99.64	1,138.11	1,369.91	844.98	2.14	0.32	812.60
Tablet06	DCL-14	120.88	149.92	1,240.23	2,139.43	1,315.78	5.68	0.32	2,147.18
	MCC	87.03	99.11	1,138.79	1,374.75	846.15	2.15	0.32	815.34
Tablet07	DCL-14	120.79	149.58	1,238.35	2,140.29	1,308.25	5.67	0.34	2,119.46
	MCC	87.25	99.38	1,138.98	1,374.28	843.12	2.15	0.33	809.65
Tablet08	DCL-14	121.03	149.82	1,237.87	2,141.84	1,315.65	5.68	0.33	2,142.67
	MCC	88.02	100.24	1,138.87	1,371.14	842.26	2.14	0.32	807.92
Tablet09	DCL-14	121.83	148.86	1,221.86	2,139.36	1,314.25	5.59	0.32	2,110.46
	MCC	87.62	99.71	1,138.01	1,368.23	840.23	2.13	0.33	803.42
Tablet10	DCL-14	120.31	149.17	1,239.88	2,139.18	1,312.41	5.67	0.33	2,135.59
	MCC	87.36	99.46	1,138.51	1,369.82	845.21	2.14	0.32	813.33

is the determined mechanical property vector based on the contact ultrasonic measurements. V, m, and ρ values are extracted from direct mass density measurements and c _L, c _T are determined from TOF ultrasonic measurements for each BL-tablet layer