Published in final edited form as: Biomaterials. 2008 Mar 4;29(15):2315–2325. doi: 10.1016/j.biomaterials.2008.01.029

Table 3.

Mechanical properties of APS polymers

Formulation Curing time (h) Young’s modulus (MPa) Elongation at break (%) UTS (MPa) Toughness (MJ m−3) n (mol m−3) Mc (g mol−1)
2DAHP–1G 24 2.45 ± 0.33 92 ± 21 1.33 ± 0.25 0.730 ± 0.31 329.24 ± 45.4 3345 ± 461
2DAHP–1G 48 4.34 ± 0.32 64 ± 12 1.69 ± 0.14 0.638 ± 0.18 583.51 ± 43.6 1879 ± 140
2DAHP–1T 24 1.45 ± 0.31 60 ± 26 0.39 ± 0.11 0.171 ± 0.18 194.90 ± 41.5 5718 ± 1218
2DAHP–1T 48 1.48 ± 0.20 21 + 2.2 0.24 ± 0.50 0.028 ± 0.008 199.16 ± 26.4 5576 ± 738