TABLE I.
Diffusivity in the entire sample |
Diffusivity in an ROI |
|||||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Glass fiber (%) |
λz (cm2/s) |
λx (cm2/s) |
λy (cm2/s) |
FA |
λz/λ⊥a | λz (cm2/s) |
λx (cm2/s) |
λy (cm2/s) |
FA |
λz/λ⊥a | ||||||||
Mean (×10−7) |
SD (×10−9) |
Mean (×10−7) |
SD (×10−9) |
Mean (×10−7) |
SD (×10−9) |
Mean | SD (×10−3) |
Mean (×10−7) |
SD (×10−9) |
Mean (×10−7) |
SD (×10−9) |
Mean (×10−7) |
SD (×10−9) |
Mean | SD (×10−3) |
|||
0 | 2.13 | 2.64 | 1.98 | 3.23 | 1.88 | 0.35 | 0.064 | 6.45 | 1.10 | 2.13 | 0.76 | 1.97 | 0.98 | 1.88 | 0.84 | 0.065 | 1.69 | 1.10 |
5 | 2.17 | 0.75 | 1.93 | 0.45 | 1.80 | 0.69 | 0.098 | 2.69 | 1.16 | 2.19 | 0.84 | 1.77 | 1.45 | 1.64 | 1.31 | 0.16 | 4.94 | 1.28 |
10 | 2.16 | 0.75 | 1.85 | 0.83 | 1.73 | 1.01 | 0.12 | 2.34 | 1.20 | 2.16 | 1.15 | 1.65 | 1.63 | 1.52 | 1.53 | 0.2 | 6.50 | 1.36 |
20 | 2.29 | 2.62 | 1.89 | 1.87 | 1.75 | 2.04 | 0.15 | 1.96 | 1.26 | 2.31 | 1.14 | 1.71 | 1.07 | 1.58 | 1.21 | 0.21 | 3.82 | 1.40 |
Measures were over the entire sample and a local ROI (see Fig. 3).
λ⊥ was calculated as the average of λx and λy.