. 2009 Mar 6;65(Pt 4):i23–i24. doi: 10.1107/S1600536809006874

Table 3. Valence-bond analysis according to the empirical expression from Brown & Altermatt (1985 ▶), using parameters for solids from Brese & O’Keeffe (1991 ▶).

  O1 O2 O3 O4 F4 F1 F2 F3 O5 Σ Σexpected
Cu 0.49 0.47 0.45 0.16 0.44         2.01 2
Fe           0.51 (× 2)  0.49 (× 2)  0.48 (× 2)    2.96  3
H11 0.80         0.20       1 1
H12 0.80           0.20     1 1
H21   0.80       0.20       1 1
H22   0.80             0.20  1 1
H31     0.80         0.20   1 1
H41       0.80     0.20     1 1
H42       0.80         0.20 1 1
H51             0.10 0.10 0.80 1 1
H52         0.20       0.80 1 1
H6         0.80 (× 0.5)         1 1
          0.20 (× 0.5)            
Σ 2.09  2.07  2.05  1.76  1.14  0.91 0.99 0.98 2.00    
Σexpected 2 2 2 2 1 1 1 1 2