Table 3.

Summary of material property measurements for the 12 pMAs (the training set). The pMAs are ordered the same way as in Figure 6–3.

	HEMA	HP	Me-EGMA	Me-HP	EGMA	Me-THFF	E-B-TEGMA	L-I-HE	O-I-HP	Isobornyl	I-B-THFF	nB-C-Undecyl
Theta	69.5	71.2	17.2	73.8	21.5	70.5	20.8	29.0	62.8	29.2	28.7	39.0
Tg	87.6	83.8	55.8	90.7	15.2	91.3	1.6	−7.7	27.3	130.2	30.9	148.9
Si2p (E)	0.1	0.3	2.0	0.1	0.5	0.2	2.2	1.0	0.5	0.4	0.3	3.0
Cls (E)	84.6	78.7	75.3	91.5	91.7	95.7	78.4	87.0	86.3	90.4	91.5	81.2
Ols (E)	15.3	21.0	22.7	8.4	7.8	4.1	19.4	12.1	13.2	9.2	8.2	15.8
Cls (T)	66.7	70.0	75.4	72.5	70.0	72.5	78.3	87.0	85.1	87.5	78.5	87.8
Ols (T)	33.3	30.0	24.6	27.5	30.0	27.5	21.7	13.0	14.9	12.5	21.5	12.2
C-C (UT)	63.9	62.3	54.9	71.7	82.2	68.5	64.7	76.8	64.5	74.5	84.0	75.8
CO (UT)	20.8	14.7	22.8	10.7	7.7	11.8	19.3	10.0	17.3	5.9	6.6	11.4
O-C=O (UT)	5.6	8.1	11.8	4.8	2.6	5.6	7.0	4.3	9.1	2.6	3.3	3.9
Beta C	9.7	11.5	10.5	12.8	7.5	13.1	9.0	9.0	7.6	14.9	6.1	4.9
C=O	0.0	3.4	0.0	0.0	0.0	1.1	0.0	0.0	1.6	2.0	0.0	4.0
C-C (GT)	73.6	76.4	64.9	84.9	88.9	75.5	73.8	89.2	70.8	87.9	91.3	90.3
CO (GT)	19.8	13.8	18.5	8.0	7.3	18.9	19.0	5.0	19.5	7.0	5.9	3.6
O-C=O (GT)	6.6	9.8	16.6	7.1	3.8	5.8	7.2	5.8	9.7	5.2	2.8	6.1
C-C(T)	0.50	0.57	0.51	0.58	0.43	0.62	0.58	0.85	0.83	0.86	0.73	0.86
CO (T)	0.33	0.29	0.33	0.27	0.43	0.14	0.31	0.09	0.10	0.07	0.12	0.07
O-C=O (T)	0.17	0.14	0.17	0.16	0.14	0.24	0.11	0.06	0.08	0.07	0.16	0.07
Ra	0.23	0.84	0.44	0.25	0.59	1.05	0.13	0.45	0.24	0.13	0.81	0.44
Sq	0.85	0.70	0.94	0.37	0.55	0.51	0.31	0.33	0.23	0.72	0.30	0.30
Ssk	1.49	0.07	1.37	−0.13	0.51	5.45	−0.53	3.68	1.84	−1.02	2.29	4.89
Sku	22.17	10.96	29.49	16.1	47.70	134.5	30.64	129.5	48.1	7.91	66.83	111.96
Sp	10.89	9.06	12.35	7.26	12.67	13.46	6.16	9.10	5.71	6.46	6.98	8.98
Sv	4.13	4.92	8.39	3.13	8.96	5.47	4.31	3.94	1.74	6.87	4.06	3.56
Sz	15.02	13.98	20.74	10.4	21.63	18.93	10.46	13.04	7.45	13.33	11.04	12.54
Sa	0.66	0.53	0.63	0.27	0.34	0.31	0.20	0.20	0.17	0.54	0.21	0.18
Sk	2.05	1.45	1.52	0.73	0.82	0.87	0.51	0.54	0.53	1.40	0.64	0.54
Spk	0.90	0.57	1.51	0.35	0.52	0.68	0.22	0.35	0.25	0.39	0.32	0.39
Svk	0.67	0.97	1.19	0.60	1.13	0.55	0.64	0.51	0.22	1.28	0.32	0.31
SMrl	11.17	9.62	13.62	10.1	9.92	10.44	9.47	10.21	10.1	7.85	10.16	10.62
SMr2	89.95	85.03	87.48	86.5	86.15	87.60	87.68	88.30	88.7	82.45	89.23	89.89
Sxp	1.73	1.30	1.52	0.63	0.70	0.75	0.43	0.45	0.45	1.24	0.55	0.45
Vvv	0.09	0.10	0.12	0.06	0.10	0.06	0.06	0.04	0.03	0.13	0.03	0.03
Vvc	1.01	0.71	0.90	0.35	0.40	0.43	0.24	0.26	0.25	0.65	0.31	0.26
Vmp	0.05	0.03	0.07	0.02	0.03	0.04	0.01	0.02	0.01	0.02	0.02	0.02
Vmc	0.72	0.59	0.62	0.28	0.31	0.32	0.19	0.19	0.19	0.59	0.23	0.19
Sal	146.1	5.61	82.17	70.5	8.29	59.30	4.14	25.59	70.9	3.10	51.71	72.18
Str	0.45	0.59	0.38	0.64	0.54	0.56	0.85	0.61	0.59	0.82	0.65	0.53