Table I.

Summary of measured detector performance of all crystals. The timing of the 1.5×1.5×40 mm³ crystal is unreliable at the central depth region, and the 6 ns is a conservative estimate of the worst timing resolution for that crystal.

Crystal Properties		DOI Resolution (mm)			Energy Resolution (%)			Timing Resolution (ns)			Peak Shifting (%)
Geometry (mm)	Surface Finish	Mean	Max	Min	Mean	Max	Min	Mean	Max	Min	Mean	Max
1.5×1.5×20	saw cut	1.5	2.0	1.2	17	19	15	2.6	2.9	2.1	15.4	26.4
1.5×1.5×20	30 µm	1.6	2.2	1.4	14	16	13	2.2	2.5	2.0	2.3	4.1
1.5×1.5×20	12 µm	2.6	3.0	2.2	14	21	13	2.4	2.6	2.2	2.2	5.8
1.5×1.5×20	9 µm	2.2	2.8	1.9	13	14	13	2.3	2.4	2.0	2.4	4.6
1.5×1.5×20	5 µm	3.3	4.4	2.1	14	16	13	2.4	2.6	2.2	2.9	7.0
1.5×1.5×20	0.5 µm	5.8	7.8	2.5	15	18	14	2.4	2.7	2.2	7.8	12.3
2.0×2.0×20	saw cut	1.6	2.1	1.2	14	16	13	2.3	2.5	2.1	2.1	3.8
2.0×2.0×20	30 µm	1.8	2.7	1.5	15	22	14	2.4	2.6	2.1	1.7	2.9
2.0×2.0×20	12 µm	2.8	4.1	2.4	13	16	12	2.2	2.4	2.1	2.3	4.7
2.0×2.0×20	9 µm	3.7	4.1	2.8	14	18	13	2.3	2.6	2.1	1.0	3.4
2.0×2.0×20	5 µm	5.9	7.3	3.9	15	16	14	2.4	2.7	2.2	4.3	6.0
2.0×2.0×20	0.5 µm	7.6	9.9	3.6	16	21	14	2.4	2.7	2.2	7.9	10.5
1.5×1.5×30	saw cut	2.4	3.9	1.9	18	21	15	3.3	5.2	2.2	23.8	40.1
1.5×1.5×40	saw cut	4.3	6.9	2.7	23	29	16	--	6.0*	2.5	36.6	57.9
2.0×2.0×30	saw cut	2.8	3.9	2.3	16	17	14	2.6	2.8	2.2	11.1	19.1
2.0×2.0×40	saw cut	3.1	5.1	2.2	16	18	13	2.6	3.3	2.0	18.0	31.2