Table 3a.
Raw Experimental Low-Temperature Molar Heat Capacities, Cp, of Starkeyite Obtained from the PPMS Experiments
| T (K) | Cp(J·K−1·mol−1) | σ-Cp(J·K−1·mol−1) |
|---|---|---|
| 5.067 | 0.059 | 0.00215 |
| 5.434 | 0.073 | 0.00182 |
| 5.828 | 0.091 | 0.00105 |
| 6.248 | 0.113 | 0.00227 |
| 6.705 | 0.142 | 0.00215 |
| 7.159 | 0.174 | 0.00163 |
| 7.671 | 0.217 | 0.00201 |
| 8.223 | 0.272 | 0.00242 |
| 8.813 | 0.342 | 0.00290 |
| 9.443 | 0.429 | 0.00353 |
| 10.118 | 0.528 | 0.03575 |
| 10.853 | 0.683 | 0.00439 |
| 11.629 | 0.861 | 0.00537 |
| 12.460 | 1.085 | 0.00652 |
| 13.352 | 1.364 | 0.00790 |
| 14.308 | 1.703 | 0.00974 |
| 15.332 | 2.130 | 0.01221 |
| 16.433 | 2.653 | 0.01441 |
| 17.610 | 3.277 | 0.01805 |
| 18.874 | 4.031 | 0.02247 |
| 20.220 | 4.937 | 0.02663 |
| 21.671 | 6.015 | 0.06166 |
| 23.225 | 7.256 | 0.05951 |
| 24.889 | 8.720 | 0.04753 |
| 26.680 | 10.420 | 0.06518 |
| 28.598 | 12.401 | 0.06576 |
| 30.655 | 14.617 | 0.07856 |
| 32.859 | 17.168 | 0.09122 |
| 35.223 | 20.024 | 0.11178 |
| 37.758 | 23.191 | 0.13084 |
| 40.474 | 26.740 | 0.15821 |
| 43.385 | 30.568 | 0.21071 |
| 46.502 | 34.702 | 0.20165 |
| 49.843 | 39.147 | 0.22764 |
| 53.427 | 43.985 | 0.25872 |
| 57.273 | 49.196 | 0.54695 |
| 61.403 | 54.461 | 0.32973 |
| 65.825 | 60.198 | 0.46813 |
| 70.558 | 66.212 | 0.41880 |
| 75.627 | 72.553 | 0.43399 |
| 81.056 | 79.155 | 0.49775 |
| 86.875 | 85.765 | 0.53520 |
| 93.112 | 92.661 | 0.57135 |
| 99.812 | 100.08 | 0.60159 |
| 106.99 | 107.78 | 0.91490 |
| 114.68 | 115.25 | 0.88310 |
| 122.94 | 123.93 | 0.73427 |
| 131.78 | 132.17 | 0.90458 |
| 141.28 | 141.61 | 1.2296 |
| 151.44 | 151.08 | 0.88392 |
| 162.40 | 161.38 | 1.2763 |
| 174.06 | 171.53 | 1.1671 |
| 186.55 | 181.95 | 1.0242 |
| 199.94 | 193.06 | 1.0749 |
| 214.26 | 203.97 | 1.6468 |
| 229.63 | 214.97 | 1.7883 |
| 246.10 | 226.99 | 1.0373 |
| 263.71 | 238.54 | 1.0712 |
| 282.55 | 250.61 | 1.1671 |
| 302.62 | 263.83 | 1.1103 |