Table 2. Dermal Film Physical Properties.

Formulation Thickness (µm) IQP-0410 (%, w/w) IQP-0410 Amount (µg/cm2) Appearance InMano evaluation
A1 50.0 2.0 294 ± 62.3 Translucent yellow Smooth; Very low tensile strength; Very high pliability
A2 100 2.0 388 ± 18.9 Translucent yellow Smooth; Very low tensile strength; Very high pliability
A3 150 2.0 481 ± 31.0 Translucent yellow Smooth; Low tensile strength; Very high pliability
A4 250 2.0 940 ± 94.4 Translucent yellow Smooth; Low tensile strength; High pliability
B1 50.0 2.0 294 ± 23.4 Translucent yellow Smooth; Very low tensile strength; Very high pliability
B2 100 2.0 386 ± 17.9 Translucent yellow Smooth; Low tensile strength; Very high pliability
B3 150 2.0 449 ± 62.1 Translucent yellow Smooth; Low tensile strength; Very high pliability
B4 250 2.0 879 ± 87.4 Translucent yellow Smooth; Low tensile strength; Moderate pliability
C1 250 2.0 907 ± 0.00 Translucent yellow Smooth; Low tensile strength; Moderate pliability
C2 400 2.0 1105 ± 16.8 Opaque yellow Smooth; Moderate tensile strength; Moderate pliability
D1 50.0 2.0 315 ± 6.57 Translucent yellow Smooth; Very low tensile strength; Very high pliability
D2 100 2.0 454 ± 14.0 Translucent yellow Smooth; Low tensile strength; Very high pliability
D3 150 2.0 448 ± 22.1 Translucent yellow Smooth; Moderate tensile strength; Very high pliability
D4 250 2.0 668 ± 54.9 Translucent yellow Smooth; Moderate tensile strength; Moderate pliability
E1 250 2.0 918 ± 98.8 Translucent yellow Smooth; Moderate tensile strength; Moderate pliability
E2 400 2.0 1168 ± 53.3 Opaque yellow Smooth; High tensile strength; Low pliability
F1 50.0 2.0 302 ± 77.3 Opaque white Rough; Very low tensile strength; High pliability
F2 100 2.0 422 ± 31.0 Opaque white Rough; Low tensile strength; High pliability
F3 150 2.0 453 ± 24.4 Opaque white Rough; Low tensile strength; High pliability
F4 250 2.0 824 ± 39.4 Opaque white Rough; Moderate tensile strength; Moderate pliability
G1 100 2.0 214 ± 50.10 Opaque white Rough; Low tensile strength; Moderate pliability
G2 250 2.0 661 ± 70.8 Opaque white Rough; Moderate tensile strength; Moderate pliability
G3 400 2.0 1225 ± 30.7 Opaque white Rough; High tensile strength; Low pliability