Figure 3.

Figure 3

Storage modulus (G’), loss modulus (G”) and conversion data vs. time for (a) the control resin (BisEMA/TEGDMA with 0.5 wt% I2959) and (b) the resin with 10 wt% nanogel solution. A 320 – 390 nm light was used for irradiation with light intensities of 0.35 mW/cm2 for the free initiator-based control and 10 mW/cm2 for nanogel-filled systems to achieve similar rates of polymerization.