| Composite Filtek P60 |
Bis-GMA |
Maximum increment of 2.5 mm, inserted in the cavity and light activated
for 40 s. |
| Shade A3 |
Bis-EMA |
|
| 3M ESPE Dental Products, MN, USA |
UDMA |
|
| N127655 |
Zirconium and silica particles (61% by volume) with sizes between 0.01
and 3.5 µm. |
|
| Composite Filtek P90 |
5-15% of 3, 4-epoxy cyclohexyl
cyclopolymethyl siloxane; |
Maximum increment of 2.5 mm, inserted
in the cavity and light activated for 40 s. |
| Shade A3 |
5-15% of 3, 4-epoxy cyclohexyl
cyclopolymethyl siloxane; |
|
| 3M ESPE Dental Products,MN, USA |
50-70% silanized quartz;10-20% Yttrium
fluoride; |
|
| N130928 |
camphorquinone. |
|
| Adper Single Bond 2 Adhesive |
Bis-GMA, HEMA, dimethacrylate ethanol, water, photoinitiators,
nanoparticles, compolymer of methacrylic acid (10%). |
Acid etching for 15 s. Rinsing for 10 s. Drying with air for 2 s.
Application of two consecutive layers of adhesive. Drying for 5 s. Light
activation for 20 s. |
| 3M ESPE Dental Products, MN, USA |
|
|
| CCBR |
|
|
| Silorane Adhesive System |
Primer: 15-25% HEMA; |
Active Primer application
for 15 seconds. Drying with air. Light activation for 10 s. Drying with
air. Application of bond. Light activation for 10 s. |
| 3M ESPE Dental Products, MN, USA |
15-25% Bis-GMA; 10-15% water; 10-15%
ethanol; 5-15% methacryl-oxy-hexyl-esters of phosphoric acid; 8-12%
silanized silica; 5-10% 1,6-hexanediol |
| 9BM/ 9BK |
dimethacrylate; <5% copolymer of
itaconic and acrylic acids; <5% (dimethylamine) ethyl methacrylate;
<3% DL-camphorquinone; <3% phosphine oxide |
|
|
Bond: 70-80% dimethacrylate
substituted; 5-10% silanized silica; 5-10% TEGDMA; <5%
methacryl-oxy-hexyl-esters of phosphoric acid; <3% DL-camphorquinone;
1,6-hexanediol Dimethacrylate; <5% copolymer of itaconic and acrylic
acids; <5% (dimethylamine) ethyl |
|