Table 1.

Means ± standard deviation for the setting time, flow, film thickness and pH of experimental sealers

	Filler concentration
	20%	40%	60%	80%	100%	120%
setting time (min)
CaWO4	451.66±4.71	430±8.17	453±8.17	509±0	501±0	448.66±11.79
YbF3	612.66±4.71	570±7.07	546.66±4.71	373±0	388±0	378±0
BaSO4	468.66±6.13	478.66±6.13	486.66±6.24	451.66±10.21	384.66±2.36	398.33±10.27
flow (mm)
CaWO4	20.26±0.51	18.92±2.16	19.28±0.57	18.10±1.28	15.02±1.81	15.85±0.25
YbF3	20.93±0.17	18.41±0.35	18.50±0.92	15.50±0.38	13.81±0.49	14.59±0.70
BaSO4	22.49±0.37	21.36±0.37	19.43±0.21	17.96±0.21	18.08±1.21	17.69±0.17
fllm thickness (pm)
CaWO4	23.33±5.77	30±0	26.67±5.77	26.67±5.77	33.33±5.77	23.33±11.55
YbF3	16.67±5.77	26.67±5.77	33.33±5.77	30±0	30±0	33.33±5.77
BaSO4	33.33±11.54	23.33±5.77	46.67±5.77	20±0	16.67±5.77	20±0
pH
CaWO4	6.31±0.13	6.69±0.08	6.66±0.08	6.82±0.08	6.84±0.05	6.99±0.03
YbF3	6.74±0.08	5.47±0.53	5.69±0.30	6.11±0.22	6.25±0.21	6.31±0.21
BaSO4	6.28±0.09	6.27±0.10	6.37±0.12	6.40±0.10	6.45±0.16	6.51±0.19