Figure 4. Advantages of the turbulent flow dispersion method for producing advanced SG-SWCNT composites.

Figure 4

SG-SWCNTs dispersed using high-pressure jet milling (100–120 MPa, 2 passes) as a turbulent flow method and thin-film spin mixing (30 m/s) as a mechanical force method for 10, 30, 60, 90, and 120 min. (a) Particle size and (b) G/D ratio of SG-SWCNTs dispersed for different times. (c) Electrical conductivity of 1 wt% SG-SWCNT/fluorinated rubber composites. (d) Level of exfoliation of SG-SWCNTs with increasing dispersion time.