Table 1.
Hydrogel Composition | Spinning Solution Concentration (wt%) | Crosslinking Method | Crosslinking Condition |
---|---|---|---|
Alginate | 0.75–3.0% Alginate 0.1–0.4% PEG |
Ionic crosslinking | 25–100 mM CaCl2 |
Fibrin + Alginate | 0.67–2.0% Fibrin 0.25–2.5% Alginate 0.1–0.2% PEG |
Enzymatic & ionic crosslinking | 5 U/ml thrombin 50 mM CaCl2 |
Gelatin + Alginate | 1.0–3.2% Gelatin 0.24–0.86% Alginate 0.40–1.0% Irgacure |
Ionic & UV-crosslinking | 50 mM CaCl2 0.50% Irgacure 10 min UV at 365 nm |
Hyaluronic Acid + Alginate | 1.0–2.0% HA 1.5% Alginate 0.1–0.4% PEG |
Ionic & Michael-Addition crosslinking | 1% PEGDA & 50 mM CaCl2 |
All hydrogel microfibres were spun at 3–5 kV electrical potential and collected in a receiving bath spun at 25–80 rpm.