Table 1. Fabricating a Ti-6Al-4V to V Gradient Alloy – Run log showing the manufacture of a gradient alloy using a blend of 325 mesh Ti-6Al-4V powder and pure V powder. The building power was 600 W, each layer is 0.38 mm thick and the total build time was 585 minutes.

Layers	% vol Ti-6Al-4V	% vol V	g/min Ti-6Al-4V	g/min V
0–28	100%	0%	2.10	0.00
29–33	97%	3%	2.04	0.08
34–38	94%	6%	1.97	0.16
39–43	91%	9%	1.91	0.24
44–48	88%	12%	1.85	0.31
49–53	85%	15%	1.79	0.39
54–58	82%	18%	1.72	0.47
59–63	79%	21%	1.66	0.55
64–68	76%	24%	1.59	0.63
69–73	73%	27%	1.53	0.71
74–78	70%	30%	1.47	0.78
79–83	67%	33%	1.41	0.86
84–88	64%	36%	1.34	0.91
89–93	61%	39%	1.28	1.02
94–98	58%	42%	1.22	1.10
99–103	55%	45%	1.16	1.18
104–108	52%	48%	1.09	1.26
109–113	49%	51%	1.57	2.03
114–118	46%	54%	1.52	2.15
119–123	43%	57%	1.42	2.27
124–128	40%	60%	1.32	2.39
129–133	37%	63%	1.22	2.51
134–138	34%	66%	1.12	2.63
139–143	31%	69%	1.02	2.75
144–148	28%	72%	0.92	2.87
149–153	25%	75%	0.83	2.99
154–158	22%	78%	0.73	3.11
159–162	19%	81%	0.62	3.23
163–166	16%	84%	0.53	3.35
167–170	13%	87%	0.43	3.47
171–174	10%	90%	0.30	3.58
175–178	7%	93%	0.23	3.71
179–182	4%	96%	0.13	3.83
183–186	1%	99%	0.03	3.94
187–195	0%	100%	0.00	3.98